|Specific energy||1,800,000 J/kg demonstrated|
|Energy density||1,260,000 J/L|
|Charge/discharge efficiency||C/5 nominal|
|Nominal cell voltage||cell voltage varies nonlinearly in the range 2.5–1.7 V during discharge; batteries often packaged for 3 V|
The lithium–sulfur battery (Li–S battery) is a type of rechargeable battery, notable for its high specific energy. The low atomic weight of lithium and moderate weight of sulfur means that Li–S batteries are relatively light (about the density of water). They were used on the longest and highest-altitude solar-powered aeroplane flight in August 2008.
Lithium–sulfur batteries may succeed lithium-ion cells because of their higher energy density and reduced cost from the use of sulfur. Currently the best Li–S batteries offer specific energies on the order of 500 W·h/kg, significantly better than most lithium-ion batteries, which are in the range of 150 to 250 W·h/kg. Li–S batteries with up to 1,500 charge and discharge cycles have been demonstrated. As of early 2014, none were commercially available. The key issue of Li–S battery is low electrical conductivity of sulfur cathode needing an extra mass for a conducting agent and the current research focus is to find highly conductive cathodes.
Chemical processes in the Li–S cell include lithium dissolution from the anode surface (and incorporation into alkali metal polysulfide salts) during discharge, and reverse lithium plating to the anode while charging. This contrasts with conventional lithium-ion cells, where the lithium ions are intercalated in the anode and cathodes. Each sulfur atom can host two lithium ions. Typically, lithium-ion batteries accommodate only 0.5–0.7 lithium ions per host atom. Consequently, Li-S allows for a much higher lithium storage density. Polysulfides are reduced on the cathode surface in sequence while the cell is discharging:
8 → Li
8 → Li
6 → Li
4 → Li
2S → Li
2 → Li
3 → Li
4 → Li
6 → Li
8 → S
These reactions are analogous to those in the sodium–sulfur battery.
The main challenges of Li-S batteries is the low conductivity of sulfur and its massive volume change upon discharging and finding a suitable cathode is the first step for commercialization of Li-S batteries. Therefore, most researchers use a carbon/sulfur cathode and a lithium anode. Sulfur is very cheap, but has practically no electroconductivity, 5×10−30 S⋅cm−1 at 25 °C. A carbon coating provides the missing electroconductivity. Carbon nanofibers provide an effective electron conduction path and structural integrity, at the disadvantage of higher cost.
One problem with the lithium–sulfur design is that when the sulfur in the cathode absorbs lithium, volume expansion of the LixS compositions happens, and predicted volume expansion of Li2S is nearly 80% of the volume of the original sulfur. This causes large mechanical stresses on the cathode, which is a major cause of rapid degradation. This process reduces the contact between the carbon and the sulfur, and prevents the flow of lithium ions to the carbon surface.
Mechanical properties of the lithiated sulfur compounds are strongly contingent on the lithium content, and with increasing lithium content, the strength of lithiated sulfur compounds improves, although this increment is not linear with lithiation.
One of the primary shortfalls of most Li–S cells is unwanted reactions with the electrolytes. While S and Li
2S are relatively insoluble in most electrolytes, many intermediate polysulfides are not. Dissolving Li
n into electrolytes causes irreversible loss of active sulfur. Use of highly reactive lithium as a negative electrode causes dissociation of most of the commonly used other type electrolytes. Use of a protective layer in the anode surface has been studied to improve cell safety, i.e., using Teflon coating showed improvement in the electrolyte stability, LIPON, Li3N also exhibited promising performance.
Because of the high potential energy density and the nonlinear discharge and charging response of the cell, a microcontroller and other safety circuitry is sometimes used along with voltage regulators to manage cell operation and prevent rapid discharge.
|Anode||Cathode||Date||Source||Specific Capacity after cycling||Notes|
|Polyethylene glycol coated, pitted mesoporous carbon||17 May 2009||University of Waterloo||1,110 mA⋅h/g after 20 cycles at a current of 168 mA⋅g−1||Minimal degradation during charge cycling. To retain polysulfides in the cathode, the surface was functionalized to repel (hydrophobic) polysulfides. In a test using a glyme solvent, a traditional sulfur cathode lost 96% of its sulfur over 30 cycles, while the experimental cathode lost only 25%.|
|Silicon nanowire||Sulfur-coated, disordered carbon nanotubes||2011||Stanford University||730 mA⋅h/g after 150 cycles (at 0.5C)||An electrolyte additive boosted the faraday efficiency from 85% to over 99%.|
|Silicon nanowire/carbon||Sulfur-coated, disordered carbon nanotubes made from carbohydrates||2013||CGS||1,300 mA⋅h/g after 400 cycles (at 1C)||Microwave processing of materials and laser-printing of electrodes.|
|Silicon carbon||Sulfur||2013||Fraunhofer Institute for Material and Beam Technology IWS||? after 1,400 cycles|
|Copolymerized sulfur||2013||University of Arizona||823 mA⋅h/g at 100 cycles||Uses "inverse vulcanization" on mostly sulfur with a small amount of 1,3-diisopropenylbenzene (DIB) additive|
2-encapsulated sulfur nanoparticles
|2013||Stanford University||721 mA⋅h/g at 1,000 cycles (0.5C)||shell protects the sulfur-lithium intermediate from electrolyte solvent. Each cathode particle is 800 nanometers in diameter. Faraday efficiency of 98.4%.|
|Sulfur||June 2013||Oak Ridge National Laboratory||1200 mA·h/g at 300 cycles at 60 °C (0.1C)
800 mA·h/g at 300 cycles at 60 °C (1C)
|Solid lithium polysulfidophosphate electrolyte. Half the voltage of typical LIBs. Remaining issues include low electrolyte ionic conductivity and brittleness in the ceramic structure.|
|Lithium||Sulfur-graphene oxide nanocomposite with styrene-butadiene-carboxymethyl cellulose copolymer binder||2013||Lawrence Berkeley National Laboratory||700 mA·h/g at 1,500 cycles (0.05C discharge)
400 mA·h/g at 1,500 cycles (0.5C charge/ 1C discharge)
|Voltage between about 1.7 and 2.5 volts, depending on charge state. Lithium bis(trifluoromethanesulfonyl)imide) dissolved in a mixture of nmethyl-(n-butyl) pyrrolidinium bis(trifluoromethanesulfonyl)-imide (PYR14TFSI), 1,3-dioxolane (DOL), dimethoxyethane (DME) with 1 M lithium bis-(trifluoromethylsulfonyl)imide (LiTFSI), and lithium nitrate (LiNO|
3). High porosity polypropylene separator. Specific energy is 500 W⋅h/kg (initial) and 250 W⋅h/kg at 1,500 cycles (C=1.0)
|Lithiated graphite||Sulfur||February 2014||Pacific Northwest National Laboratory||400 cycles||Coating prevents polysulfides from destroying the anode.|
|Lithiated graphene||Sulfur/Lithium-sulfide passivation layer||2014||OXIS Energy||240 mA·h/g (1000 cycles)
|Passivation layer prevents sulfur loss|
|Lithium sulfur batteries||Carbon nanotube/Sulfur||2014||Tsinghua University ||15.1 mA·h⋅cm−2 at a sulfur loading of 17.3 mgS⋅cm−2||A free-standing CNT–S paper electrode with a high areal sulfur-loading was fabricated, in which short MWCNTs served as the short-range electrical conductive network and super-long CNTs acted as both the long-range conductive network and intercrossed binders.|
|Glass-coated sulfur with mildly reduced graphene oxide for structural support||2015||University of California, Riverside||700 mA⋅h⋅g−1 (50 cycles)||Glass coating prevents lithium polysulfides from permanently migrating to an electrode|
|Lithium||Sulfur||2016||LEITAT||500 W⋅h/kg||ALISE H2020 project developing a Li-S battery for cars with new components and optimized regarding anode, cathode, electrolyte and separator|
As of 2015 few companies had been able to commercialize the technology on an industrial scale. Companies such as Sion Power have partnered with Airbus Defence and Space to test their lithium sulfur battery technology. Airbus Defense and Space successfully launched their prototype High Altitude Pseudo-Satellite (HAPS) aircraft powered by solar energy during the day and by lithium sulfur batteries at night in real life conditions during an 11-day flight. The batteries used in the test flight utilized Sion Power's Li-S cells that provide 350 W⋅h/kg. Sion claims to be in the process of volume manufacturing with availability by end of 2017.
British firm OXIS Energy developed prototype lithium sulfur batteries that are currently operating in small scale, commercial, test applications. As of June 2015, OXIS Energy planned to sell its energy storage batteries from 2016. Together with Imperial College London and Cranfield University, OXIS Energy published equivalent-circuit-network models for its cells. With Lithium Balance of Denmark they built a prototype scooter battery system primarily for the Chinese market. The prototype battery has a capacity of 1.2kWh using 10Ah OXIS Long Life cells, weighs 60% less than lead acid batteries with a significant increase in range. OXIS Energy has built a 3U, 3,000 W⋅h Rack-Mounted Battery that weighs only 25 kg and is fully scalable. OXIS anticipates that its Lithium-Sulfur batteries will cost about $200/kWh in mass production. OXIS has also been involved in the European Consortium for Lithium-Sulphur Power for Space Environments (ECLIPSE) H2020 project. This project is developing high-capacity Li-S batteries for satellites and launchers.
- Zhang, Sheng S (2013). "Liquid electrolyte lithium/sulfur battery: Fundamental chemistry, problems, and solutions". Journal of Power Sources. 231: 153–162. doi:10.1016/j.jpowsour.2012.12.102.
- Amos, J. (24 August 2008) "Solar plane makes record flight" BBC News
- Arumugam Manthiram, Yongzhu Fu, Yu-Sheng Su "Challenges and Prospects of Lithium–Sulfur Batteries" Acc. Chem. Res., 2013, volume 46, pp 1125–1134. doi:10.1021/ar300179v
- "OXIS Energy's Lithium-Sulfur Battery Technology". Retrieved 2017-05-20.
- "New lithium/sulfur battery doubles energy density of lithium-ion". Gizmag.com. Retrieved 2014-02-18.
- Eftekhari, Ali (2017). "The rise of lithium–selenium batteries". Sustainable Energy & Fuels. 1: 14–29. doi:10.1039/C6SE00094K.
- Tudron, F.B., Akridge, J.R., and Puglisi, V.J. (2004) "Lithium-Sulfur Rechargeable Batteries: Characteristics, State of Development, and Applicability to Powering Portable Electronics" (Tucson, AZ: Sion Power)
- Bullis, Kevin (May 22, 2009). "Revisiting Lithium-Sulfur Batteries". Technology Review. Retrieved August 12, 2016.
- Eftekhari, A. (2017). "Cathode Materials for Lithium–Sulfur Batteries: A Practical Perspective". Journal of Materials Chemistry A. 5 (34): 17734–17776. doi:10.1039/C7TA00799J.
- Choi, Y.J.; Kim, K.W. (2008). "Improvement of cycle property of sulfur electrode for lithium/sulfur battery". Journal of Alloys and Compounds. 449: 313–316. doi:10.1016/j.jallcom.2006.02.098.
- J.A. Dean, ed. (1985). Lange's Handbook of Chemistry (third ed.). New York: McGraw-Hill. pp. 3–5.
- Choi, Y. J.; Chung, Y. D.; Baek, C. Y.; Kim, K. W.; Ahn, J. H. (March 4, 2008). "Effects of carbon coating on the electrochemical properties of sulfur cathode for lithium/sulfur cell". J. Power Sources. 184 (2): 548–552. Bibcode:2008JPS...184..548C. doi:10.1016/j.jpowsour.2008.02.053.
- Islam, Md Mahbubul; Ostadhossein, Alireza; Borodin, Oleg; Yeates, A. Todd; Tipton, William W.; Hennig, Richard G.; Kumar, Nitin; Duin, Adri C. T. van (2015-01-21). "ReaxFF molecular dynamics simulations on lithiated sulfur cathode materials". Phys. Chem. Chem. Phys. 17 (5): 3383–3393. Bibcode:2015PCCP...17.3383I. doi:10.1039/c4cp04532g. PMID 25529209.
- Brian Dodson, "New lithium/sulfur battery doubles energy density of lithium-ion", gizmag, 1 December 2013
- Islam; et al. (2015). "ReaxFF molecular dynamics simulations on lithiated sulfur cathode materials". Phys. Chem. Chem. Phys. 17 (5): 3383–3393. Bibcode:2015PCCP...17.3383I. doi:10.1039/C4CP04532G. PMID 25529209.
- Jeong, S. S.; Lim, Y.; Choi, Y. T.; Kim, K. W.; Ahn, H. J.; Cho, K. K. (2006). "Electrochemical properties of lithium sulfur cells using PEO polymer electrolytes prepared under three different mixing conditions". J. Power Sources. 174 (2): 745–750. Bibcode:2007JPS...174..745J. doi:10.1016/j.jpowsour.2007.06.108.
- Islam, Md Mahbubul; Bryantsev, Vyacheslav S.; van Duin, Adri CT (2014). "ReaxFF Reactive Force Field Simulations on the Influence of Teflon on Electrolyte Decomposition during Li/SWCNT Anode Discharge in Lithium-Sulfur Batteries". Journal of the Electrochemical Society. 161 (8): E3009–E3014. doi:10.1149/2.005408jes.
- Akridge, J.R. (October 2001) "Lithium Sulfur Rechargeable Battery Safety" Battery Power Products & Technology
- Xiulei Ji, Kyu Tae Lee, and Linda F. Nazar. (17 May 2009)"A highly ordered nanostructured carbon-sulphur cathode for lithium-sulphur batteries." Nature Materials
- Guangyuan, Zheng; Yuan Yang; Judy J. Cha; Seung Sae Hong; Yi Cui (14 September 2011). "Hollow Carbon Nanofiber-Encapsulated Sulfur Cathodes for High Specific Capacity Rechargeable Lithium Batteries". Nano Letters. 11 (10): 4462–4467. Bibcode:2011NanoL..11.4462Z. doi:10.1021/nl2027684. PMID 21916442.
- Keller, Sarah Jane (October 4, 2011). "Sulfur in hollow nanofibers overcomes challenges of lithium-ion battery design". Stanford News. Stanford University. Retrieved February 18, 2012.
- Rosenberg, Sarah; Hintennach (1 April 2014). "Laser-printed lithium-sulphur micro-electrodes for Li/S batteries". Russian Journal of Electrochemistry: 327–335.
- Vandenberg, Aurelius; Hintennach (1 April 2014). "A novel design approach for lithium-sulphur batteries". Russian Journal of Electrochemistry: 317–326.
- "Researchers increase lifespan of lithium-sulfur batteries". Gizmag.com. Retrieved 2013-12-04.
- Chung, W. J.; Griebel, J. J.; Kim, E. T.; Yoon, H.; Simmonds, A. G.; Ji, H. J.; Dirlam, P. T.; Glass, R. S.; Wie, J. J.; Nguyen, N. A.; Guralnick, B. W.; Park, J.; Somogyi, Á. D.; Theato, P.; MacKay, M. E.; Sung, Y. E.; Char, K.; Pyun, J. (2013). "The use of elemental sulfur as an alternative feedstock for polymeric materials". Nature Chemistry. 5 (6): 518–524. Bibcode:2013NatCh...5..518C. doi:10.1038/nchem.1624. PMID 23695634.
- Caryl Richards (2013-04-16). "Radical approach to turn sulfur into polymers".
- SLAC National Accelerator Laboratory (6 Posts) (2013-01-08). "World-Record Battery Performance Achieved With Egg-Like Nanostructures". CleanTechnica. Retrieved 2013-06-11.
- Wei Seh, Z.; Li, W.; Cha, J. J.; Zheng, G.; Yang, Y.; McDowell, M. T.; Hsu, P. C.; Cui, Y. (2013). "Sulphur–TiO2 yolk–shell nanoarchitecture with internal void space for long-cycle lithium–sulphur batteries". Nature Communications. 4: 1331. Bibcode:2013NatCo...4E1331W. doi:10.1038/ncomms2327. PMID 23299881.
- Lin, Z; Liu, Z; Fu, W; Dudney, NJ; Liang, C (2013). "Lithium Polysulfidophosphates: A Family of Lithium-Conducting Sulfur-Rich Compounds for Lithium–Sulfur Batteries". Angewandte Chemie International Edition. 52 (29): 7460–7463. doi:10.1002/anie.201300680. PMID 23737078.
- Lin, Z.; Liu, Z.; Fu, W.; Dudney, N. J.; Liang, C. (2013). "Lithium Polysulfidophosphates: A Family of Lithium-Conducting Sulfur-Rich Compounds for Lithium-Sulfur Batteries". Angewandte Chemie International Edition. 52 (29): 7460–7463. doi:10.1002/anie.201300680. PMID 23737078.
- "All-solid lithium-sulfur battery stores four times the energy of lithium-ions". Gizmag.com. Retrieved 2013-06-13.
- "New lithium/sulfur battery doubles energy density of lithium-ion". Gizmag.com. Retrieved 2013-12-04.
- Lavars, Nick (February 20, 2014). "Hybrid anode quadruples the lifespan of lithium-sulfur batteries". Retrieved August 22, 2016.
- "A whiff of brimstone". Economist. January 3, 2015. Retrieved August 22, 2016.
- "Li-S battery company OXIS Energy reports 300 W⋅h/kg and 25 A⋅h cell, predicting 33 A⋅h by mid-2015, 500 W⋅h/kg by end of 2018". Green Car Congress. November 12, 2014. Retrieved August 22, 2016.
- Yuan, Zhe; Peng, Hong-Jie; Huang, Jia-Qi; Liu, Xin-Yan; Wang, Dai-Wei; Cheng, Xin-Bing; Zhang, Qiang (2014-10-01). "Hierarchical Free-Standing Carbon-Nanotube Paper Electrodes with Ultrahigh Sulfur-Loading for Lithium–Sulfur Batteries". Advanced Functional Materials. 24 (39): 6105–6112. doi:10.1002/adfm.201401501. ISSN 1616-3028.
- Nealon, Sean (2015-03-03). "Glass coating for improved battery performance". R&D. Retrieved August 22, 2016.
- Nealon, Sean (March 2, 2015). "Glass coating improves battery performance". phys.org. Retrieved August 22, 2016.
- Kopera, J (September 2014) "Sion Power's Lithium-Sulfur Batteries Power High Altitude Pseudo-Satellite Flight" Sion Power Company Press Release
- "Sion Power Delivers Next Generation Battery Performance Through Patented Licerion® Technology". 2016-10-03. Retrieved 4 October 2016.
- "Anesco and OXIS to Release Lithium Sulfur Battery Storage by 2016" (press release). OXIS Energy. July 14, 2015. Retrieved August 22, 2016.
- "OXIS battery powers driverless vehicle for the UK Government's Smart City Gateway programme" (press release). OXIS Energy. February 22, 2015. Retrieved August 22, 2016.
- Propp, K.; Marinescu, M.; Auger, D. J.; et al. (August 12, 2016). "Multi-temperature state-dependent equivalent circuit discharge model for lithium-sulfur batteries". J. Power Sources. 328: 289–299. Bibcode:2016JPS...328..289P. doi:10.1016/j.jpowsour.2016.07.090.
- "Lithium Sulfur batteries will be first commercialized by 2018 in electric bikes where energy density will be improved for eventual use in electric cars". www.nextbigfuture.com. 2016-06-10. Retrieved 2017-02-02.
- "OXIS Rack-Mounted Battery" (PDF). OXIS Energy. Retrieved May 20, 2017.
- "OXIS Energy Lithium-Sulfur Battery Technology Presentation". OXIS Energy. 2016-11-03. Retrieved May 20, 2017.
- "ECLIPSE project". ECLIPSE. Retrieved May 26, 2017.
- "Sony battery to offer 40% longer phone life". Nikkei Asian Review. December 17, 2015. Retrieved August 22, 2016.
- "OXIS Energy". OXIS Energy. Retrieved 2013-10-30.
- "PolyPlus Lithium Sulfur". Polyplus.com. Archived from the original on 2013-04-20. Retrieved 2013-04-06.
- "Sion Power". Sion Power. Retrieved 2013-04-06.
- "Winston Battery Limited". En.winston-battery.com. Retrieved 2013-04-06.
- "EEMB Battery". EEMB Battery. Retrieved 2018-04-13.