|Systematic IUPAC name
3D model (JSmol)
|Molar mass||276 g·mol−1|
|Appearance||Dark yellow crystals|
|Density||11.5 g cm−3|
|Melting point||2,744 °C (4,971 °F; 3,017 K)|
|Boiling point||2,800 °C (5,070 °F; 3,070 K)|
|Fluorite (cubic), cF12|
|Fm3m, No. 225|
|Tetrahedral (O2−); cubic (PuIV)|
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|what is ?)(|
Plutonium(IV) oxide is the chemical compound with the formula PuO2. This high melting-point solid is a principal compound of plutonium. It can vary in color from yellow to olive green, depending on the particle size, temperature and method of production.
PuO2 crystallizes in the fluorite motif, with the Pu4+ centers organized in a face-centered cubic array and oxide ions occupying tetrahedral holes. PuO2 owes its utility as a nuclear fuel to the fact that vacancies in the octahedral holes allows room for fission products. In nuclear fission, one atom of plutonium splits into two. The vacancy of the octahedral holes provides room for the new product and allows the PuO2 monolith to retain its structural integrity.
Plutonium dioxide is a stable ceramic material with an extremely low solubility in water and with a high melting point (2,744 °C). The melting point was revised upwards in 2011 by several hundred degrees, based on evidence from rapid laser melting studies which avoid contamination by any container material.
Plutonium metal spontaneously oxidizes to PuO2 in an atmosphere of oxygen. Plutonium dioxide is mainly produced by calcination of plutonium(IV) oxalate, Pu(C2O4)2·6H2O, at 300 °C. Plutonium oxalate is obtained during the reprocessing of nuclear fuel as plutonium is dissolved in HNO3/HF. Plutonium dioxide can also be recovered from molten-salt breeder reactors by adding sodium carbonate to the fuel salt after any remaining uranium is removed from the salt as its hexafluoride.
PuO2, along with UO2, is used in MOX fuels for nuclear reactors. Plutonium-238 dioxide is used as fuel for several deep-space spacecraft such as the 'New Horizons' Pluto probe as well as in the Curiosity rover on Mars. The isotope decays by emitting α-particles, which then generate heat (see radioisotope thermoelectric generator). There have been concerns that an accidental re-entry into Earth's atmosphere from orbit might lead to the break-up and/or burn-up of a spacecraft, resulting in the dispersal of the plutonium, either over a large tract of the planetary surface or within the upper atmosphere. However, although at least two spacecraft carrying PuO2 RTGs have reentered the Earth's atmosphere and burned up (Nimbus B-1 in May 1968 and the Apollo 13 Lunar Module in April 1970), the RTGs from both spacecraft survived reentry and impact intact, and no environmental contamination was noted in either instance; in any case, RTGs since the mid-1960s have been designed to remain intact in the event of reentry and impact, following the 1964 launch failure of Transit 5-BN-3 (the early-generation plutonium-metal RTG on board disintegrated upon reentry and dispersed radioactive material into the atmosphere north of Madagascar, prompting a redesign of all U.S. RTGs then in use or under development).
Physicist Peter Zimmerman, following up a suggestion by Ted Taylor, demonstrated that a low-yield (1-kiloton) nuclear weapon could be made relatively easily from plutonium oxide. A plutonium-oxide bomb would have a considerably larger critical mass than one made from plutonium metal (almost three times larger, even with the oxide at maximum crystal density; if the oxide were in powder form, as is often encountered, the critical mass would be much higher still), due both to the lower density of plutonium in PuO2 compared with plutonium metal and to the added inert mass of the oxygen contained.
The behavior of plutonium oxide in the body varies with the way in which it is taken. Since it is insoluble, when ingested, a very large percentage of it will be eliminated from the body quite rapidly in body wastes. In particulate form, plutonium oxide at a particle size less than 10 micrometers (0.01 mm) is toxic if inhaled, due to its alpha-emission.
- "Nitric acid processing". Los Alamos Laboratory.
- Greenwood, Norman N.; Earnshaw, Alan (1984). Chemistry of the Elements. Oxford: Pergamon Press. p. 1471. ISBN 978-0-08-022057-4.
- De Bruycker, F.; Boboridis, K.; Pöml, P.; Eloirdi, R.; Konings, R. J. M.; Manara, D. "The melting behaviour of plutonium dioxide: A laser-heating study". Journal of Nuclear Materials. 416 (1–2): 166–172. Bibcode:2011JNuM..416..166D. doi:10.1016/j.jnucmat.2010.11.030.
- Jeffrey A. Katalenich Michael R. Hartman Robert C. O’Brien Steven D. Howe (Feb 2013). "Fabrication of Cerium Oxide and Uranium Oxide Microspheres for Space Nuclear Power Applications" (PDF). Proceedings of Nuclear and Emerging Technologies for Space 2013: 2.
- A. Angelo Jr. and D. Buden (1985). Space Nuclear Power. Krieger Publishing Company. ISBN 0-89464-000-3.
- "General Safety Considerations" (PDF lecture notes). Fusion Technology Institute, University of Wisconsin–Madison. Spring 2000.
- "Transit". Encyclopedia Astronautica. Retrieved 2013-05-07.
- Michael Singer; David Weir & Barbara Newman Canfield (Nov 26, 1979). "Nuclear Nightmare: America's Worst Fear Come True". New York Magazine.
- Sublette, Carey. "4.1 Elements of Fission Weapon Design". The Nuclear Weapon Archive. 126.96.36.199.2.1 Plutonium Oxide. Retrieved 20 October 2017.
The critical mass of reactor grade plutonium is about 13.9 kg (unreflected), or 6.1 kg (10 cm nat. U) at a density of 19.4. A powder compact with a density of 8 would thus have a critical mass that is (19.4/8)^2 time higher: 82 kg (unreflected) and 36 kg (reflected), not counting the weight of the oxygen (which adds another 14%). If compressed to crystal density these values drop to 40 kg and 17.5 kg.
- United States Nuclear Regulatory Commission, Fact sheet on plutonium (accessed Nov 29 2013)
- World Nuclear Society, Plutonium (accessed Nov 29 2013)
- "Toxicological Profile For Plutonium" (PDF). U.S. Department of Health and Human Services. 2007-09-27. Retrieved 2009-04-23.